1.1 These four test methods cover the determination of the strength of intact rock core specimens in uniaxial and triaxial compression. Methods A and B determine the triaxial compressive strength at different pressures and Methods C and D determine the unconfined, uniaxial strength. 1.2 Methods A and B can be used to determine the angle of internal friction, angle of shearing resistance, and cohesion intercept. 1.3 Methods B and D specify the apparatus, instrumentation, and procedures for determining the stress-axial strain and the stress-lateral strain curves, as well as Young's modulus, E , and Poisson's ratio, u. These methods make no provision for pore pressure measurements and specimens are undrained (platens are not vented). Thus, the strength values determined are in terms of total stress and are not corrected for pore pressures. These test methods do not include the procedures necessary to obtain a stress-strain curve beyond the ultimate strength. 1.4 Option A allows for testing at different temperatures and can be applied to any of the test methods, if requested. 1.5 This standard replaces and combines the following Standard Test Methods: D2664 Triaxial Compressive Strength of Undrained Rock Core Specimens Without Pore Pressure Measurements; D5407 Elastic Moduli of Undrained Rock Core Specimens in Triaxial Compression Without Pore Pressure Measurements; D2938 Unconfined Compressive Strength of Intact Rock Core Specimens; and D3148 Elastic Moduli of Intact Rock Core Specimens in Uniaxial Compression. The original four standards are now referred to as Methods in this standard. 1.5.1 Method A: Triaxial Compressive Strength of Undrained Rock Core Specimens Without Pore Pressure Measurements. 1.5.1.1 Method A is used for obtaining strength determinations. Strain is not typically measured; therefore a stress-strain curve is not produced. 1.5.2 Method B: Elastic Moduli of Undrained Rock Core Specimens in Triaxial Compression Without Pore Pressure Measurements. 1.5.3 Method C: Uniaxial Compressive Strength of Intact Rock Core Specimens. 1.5.3.1 Method C is used for obtaining strength determinations. Strain is not typically measured; therefore a stress-strain curve is not produced. 1.5.4 Method D: Elastic Moduli of Intact Rock Core Specimens in Uniaxial Compression. 1.5.5 Option A: Temperature Variation- Applies to any of the methods and allows for testing at temperatures above or below room temperature. 1.6 For an isotropic material in Test Methods B and D, the relation between the shear and bulk moduli and Young's modulus and Poisson's ratio are: where: G = shear modulus, K = bulk modulus, E = Young's modulus, and u = Poisson's ratio. 1.6.1 The engineering applicability of these equations decreases with increasing anisotropy of the rock. It is desirable to conduct tests in the plane of foliation, cleavage or bedding and at right angles to it to determine the degree of anisotropy. It is noted that equations developed for isotropic materials may give only approximate calculated results if the difference in elastic moduli in two orthogonal directions is greater than 10% for a given stress level. Note 1 - Elastic moduli measured by sonic methods (Test Method D2845) may often be employed as a preliminary measure of anisotropy. 1.7 Test Methods B and D for determining the elastic constants do not apply to rocks that undergo significant inelastic strains during the test, such as potash and salt. The elastic moduli for such rocks should be determined from unload-reload cycles that are not covered by these test methods. 1.8 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard. 1.9 All observed and calculated values shall conform to the guidelines for significant digits and rounding established in Practice D6026. 1.9.1 The procedures used to specify how data are collected/recorded or calculated, in this standard are regarded as the industry standard. In addition, they are representative of the significant digits that generally should be retained. The procedures used do not consider material variation, purpose for obtaining the data, special purpose studies, or any considerations for the user's objectives; and it is common practice to increase or reduce significant digits of reported data to be commensurate with these considerations. It is beyond the scope of this standard to consider significant digits used in analytical methods for engineering design. 1.10 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.