Rubbers; Determination of crystallization effects by hardness measurements

ISO 3387

Số trang: 5
Ngày phát hành: 1978-11-00

Liên hệ

Tóm tắt
Chi tiết

Describes a test based on the progressive stiffening of rubber with time, caused by crystallization. It is limited to materials having an initial hardness at test temperature of 10 to 85 IRHD. The method is applicable to raw, unvulcanized (compounded), and vulcanized rubber. It is mainly of interest for rubber with a marked crystallization tendency at temperatures experienced in cold climates, such as, for instance, chloroprene and natural rubber. The method is not applicable to fast-crystallizing materials.

Số hiệu tiêu chuẩn

ISO 3387

Tên tiêu chuẩn

Rubbers; Determination of crystallization effects by hardness measurements

Ngày phát hành

1978-11-00

Trạng thái

Hết hiệu lực

Tiêu chuẩn tương đương

DIN 53541 (1980-01), MOD * BS 5294 (1976-02-27), NEQ * NF T46-027 (1976-11-01), IDT * UNE 53631 (1989-10-24), IDT * TS 6687 (1989-03-14), IDT * DS/ISO 3387 (1982), IDT * NBN T 31-034 (1980), IDT * NEN-ISO 3387 (1980), IDT * UNI 8830 (1985), IDT * NEN-ISO 3387:1980 en (1980-11-01), IDT

Tiêu chuẩn liên quan

Thay thế cho

Thay thế bằng

ISO 3387 (1994-06)

Lịch sử ban hành

ISO 3387 (1994-06) * ISO 3387 (1978-11) * ISO 3387 (2012-07)

Từ khóa

Ageing (materials) * Crystallization * Hardness measurement * Rubber * Test specimens * Testing * Tests * Vulcanized rubber * Unworked

Mục phân loại

83.060. Cao su

Số trang

LOẠI TIÊU CHUẨN PHỔ BIẾN | TẤT CẢ LOẠI TIÊU CHUẨN

Rubber - Determination of crystallization effects by hardness measurements
Số hiệu tiêu chuẩn	ISO 3387
Ngày phát hành	1994-06-00
Mục phân loại	83.060. Cao su
Trạng thái	Có hiệu lực

Rubbers; Determination of crystallization effects by hardness measurements
Số hiệu tiêu chuẩn	ISO 3387
Ngày phát hành	1978-11-00
Mục phân loại	83.060. Cao su
Trạng thái	Có hiệu lực