ASTM G 67

Standard Test Method for Determining the Susceptibility to Intergranular Corrosion of 5XXX Series Aluminum Alloys by Mass Loss After Exposure to Nitric Acid (NAMLT Test)

Số trang: 3
Ngày phát hành: 1999-00-00

Liên hệ
1.1 This test method describes a procedure for constant immersion intergranular corrosion testing of 5XXX series aluminum alloys. 1.2 This test method is applicable only to wrought products. 1.3 This test method covers type of specimen, specimen preparation, test environment, and method of exposure. 1.4 The values stated in SI units are to be regarded as the standard. 1.5 This standard does not purport to address all of the safety problems, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
Số hiệu tiêu chuẩn
ASTM G 67
Tên tiêu chuẩn
Standard Test Method for Determining the Susceptibility to Intergranular Corrosion of 5XXX Series Aluminum Alloys by Mass Loss After Exposure to Nitric Acid (NAMLT Test)
Ngày phát hành
1999-00-00
Trạng thái
Hết hiệu lực
Tiêu chuẩn tương đương
Tiêu chuẩn liên quan
Thay thế cho
ASTM G 67 (1993)
Test Method for Determining the Susceptibility to Intergranular Corrosion of 5XXX Series Aluminum Alloys by Mass Loss After Exposure to Nitric Acid (NAMLT Test)
Số hiệu tiêu chuẩn ASTM G 67
Ngày phát hành 1993-00-00
Mục phân loại 77.120.10. Nhôm và hợp kim nhôm
Trạng thái Có hiệu lực
Thay thế bằng
ASTM G 67 (2004)
Standard Test Method for Determining the Susceptibility to Intergranular Corrosion of 5XXX Series Aluminum Alloys by Mass Loss After Exposure to Nitric Acid (NAMLT Test)
Số hiệu tiêu chuẩn ASTM G 67
Ngày phát hành 2004-00-00
Mục phân loại 77.120.10. Nhôm và hợp kim nhôm
Trạng thái Có hiệu lực
Lịch sử ban hành
ASTM G 67 (2004)
Standard Test Method for Determining the Susceptibility to Intergranular Corrosion of 5XXX Series Aluminum Alloys by Mass Loss After Exposure to Nitric Acid (NAMLT Test)
Số hiệu tiêu chuẩn ASTM G 67
Ngày phát hành 2004-00-00
Mục phân loại 77.120.10. Nhôm và hợp kim nhôm
Trạng thái Có hiệu lực
* ASTM G 67 (1999)
Standard Test Method for Determining the Susceptibility to Intergranular Corrosion of 5XXX Series Aluminum Alloys by Mass Loss After Exposure to Nitric Acid (NAMLT Test)
Số hiệu tiêu chuẩn ASTM G 67
Ngày phát hành 1999-00-00
Mục phân loại 77.120.10. Nhôm và hợp kim nhôm
Trạng thái Có hiệu lực
* ASTM G 67 (1993)
Test Method for Determining the Susceptibility to Intergranular Corrosion of 5XXX Series Aluminum Alloys by Mass Loss After Exposure to Nitric Acid (NAMLT Test)
Số hiệu tiêu chuẩn ASTM G 67
Ngày phát hành 1993-00-00
Mục phân loại 77.120.10. Nhôm và hợp kim nhôm
Trạng thái Có hiệu lực
* ASTM G 67 (1986)
Test Method for Determining the Susceptibility to Intergranular Corrosion of 5XXX Series Aluminum Alloys by Mass Loss After Exposure to Nitric Acid (NAMLT Test)
Số hiệu tiêu chuẩn ASTM G 67
Ngày phát hành 1986-00-00
Mục phân loại 77.060. Ăn mòn kim loại
77.120.10. Nhôm và hợp kim nhôm
Trạng thái Có hiệu lực
* ASTM G 67 (1980)
Test Method for Determining the Susceptibility to Intergranular Corrosion of 5XXX Series Aluminum Alloys by Mass Loss After Exposure to Nitric Acid (NAMLT Test)
Số hiệu tiêu chuẩn ASTM G 67
Ngày phát hành 1980-00-00
Mục phân loại 77.060. Ăn mòn kim loại
77.120.10. Nhôm và hợp kim nhôm
Trạng thái Có hiệu lực
Từ khóa
Alloys * Aluminium * Corrosion * Determination * Intergranular corrosion * Metals * Nitric acid * Susceptibility * Testing * Wear
Số trang
3