Standard Test Methods for Rubber Property - Stiffening at Low Temperatures: Flexible Polymers and Coated Fabrics

Số trang: 9
Ngày phát hành: 1992-00-00

Liên hệ
1.1 These test methods describe the use of a torsional apparatus for measuring the relative low temperature stiffening of flexible polymeric materials and fabrics coated therewith. A routine inspection and acceptance procedure, to be used as a pass-fail test at a specified temperature, is also described. 1.2 These test methods yield comparative data to assess the low temperature performance of flexible polymers and fabrics coated therewith. 1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
Số hiệu tiêu chuẩn
ASTM D 1053a
Tên tiêu chuẩn
Standard Test Methods for Rubber Property - Stiffening at Low Temperatures: Flexible Polymers and Coated Fabrics
Ngày phát hành
1992-00-00
Trạng thái
Có hiệu lực
Tiêu chuẩn tương đương
Tiêu chuẩn liên quan
Thay thế cho
ASTM D 1053 (1992)
Standard Test Methods for Rubber Property-Stiffening at Low Temperatures Flexible Polymers and Coated Fabrics
Số hiệu tiêu chuẩn ASTM D 1053
Ngày phát hành 1992-00-00
Mục phân loại 83.060. Cao su
Trạng thái Có hiệu lực
Thay thế bằng
Lịch sử ban hành
ASTM D 1053 (1992)
Standard Test Methods for Rubber Property-Stiffening at Low Temperatures Flexible Polymers and Coated Fabrics
Số hiệu tiêu chuẩn ASTM D 1053
Ngày phát hành 1992-00-00
Mục phân loại 83.060. Cao su
Trạng thái Có hiệu lực
* ASTM D 1053 (1989)
Test Methods for Rubber Property - Stiffening at Low Temperatures: Flexible Polymers and Coated Fabrics
Số hiệu tiêu chuẩn ASTM D 1053
Ngày phát hành 1989-00-00
Mục phân loại 83.060. Cao su
Trạng thái Có hiệu lực
* ASTM D 3388 (1981)
Method of Testing Coated Fabrics-Stiffening at Low Temperatures (Torsional Wire Apparatus)
Số hiệu tiêu chuẩn ASTM D 3388
Ngày phát hành 1981-00-00
Mục phân loại 83.060. Cao su
Trạng thái Có hiệu lực
* ASTM D 1053a (1992)
Standard Test Methods for Rubber Property - Stiffening at Low Temperatures: Flexible Polymers and Coated Fabrics
Số hiệu tiêu chuẩn ASTM D 1053a
Ngày phát hành 1992-00-00
Mục phân loại 83.060. Cao su
Trạng thái Có hiệu lực
* ASTM D 1053 (1985)
Test Method for Rubber Property -Stiffening at Low Temperatures: Flexible Polymers and Coated Fabrics
Số hiệu tiêu chuẩn ASTM D 1053
Ngày phát hành 1985-00-00
Mục phân loại 83.060. Cao su
Trạng thái Có hiệu lực
* ASTM D 1053a (1989)
Test Methods for Rubber Property - Stiffening at Low Temperatures: Flexible Polymers and Coated Fabrics
Số hiệu tiêu chuẩn ASTM D 1053a
Ngày phát hành 1989-00-00
Mục phân loại 83.060. Cao su
Trạng thái Có hiệu lực
Từ khóa
Carbon black * Coated fabrics * Fabrics * Low temperatures * Natural rubber * Polymers * Properties * Rubber * Stiffening * Stiffness * Synthetic rubber * Testing * Torsion * Netting * Tissue
Mục phân loại
Số trang
9