ASTM A 90/A 90Ma

Standard Test Method for Weight [Mass] of Coating on Iron and Steel Articles with Zinc or Zinc-Alloy Coatings

Số trang: 4
Ngày phát hành: 1995-00-00

Liên hệ
1. Scope 1.1 This test method covers procedures for determining the weight [mass] of coating on iron or steel sheet, wire, and other articles in which the coating is zinc or a zinc alloy, such as zinc-5% aluminum (including zinc-5% aluminum-mischmetal and zinc-5% aluminum-0.1% magnesium) or 55% aluminum-zinc. In the body of this test method, reference to zinc coating shall be interpreted to also include zinc alloy coating except where specifically stated otherwise. 1.2 The final results determined by this test method shall be expressed in inch-pound units or SI units, depending on the units used in the material specification to which the results are to be compared. Certain portions of the procedure involving determination of specimen weight [mass] have traditionally been performed in SI units, and corresponding inch-pound units are not included. 1.3 In this test method, the quantity of material is described in terms of weight [mass]. Weight is the force describing the gravitational attraction of the earth on a quantity of material. In general usage on the surface of the earth, mass of an unknown quantity is determined by comparing with a known quantity (either directly or indirectly and ignoring the buoyancy of the air) as indicated by the attraction of the earths gravity, thus weight is actually determined. See Appendix X1 of Terminology E12 for further discussion of weight and mass. 1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. For specific hazards statements see 5.1.
Số hiệu tiêu chuẩn
ASTM A 90/A 90Ma
Tên tiêu chuẩn
Standard Test Method for Weight [Mass] of Coating on Iron and Steel Articles with Zinc or Zinc-Alloy Coatings
Ngày phát hành
1995-00-00
Trạng thái
Hết hiệu lực
Tiêu chuẩn tương đương
Tiêu chuẩn liên quan
Thay thế cho
ASTM A 90/A 90M (1995)
Standard Test Method for Weight [Mass] of Coating on Iron and Steel Articles with Zinc or Zinc-Alloy Coatings
Số hiệu tiêu chuẩn ASTM A 90/A 90M
Ngày phát hành 1995-00-00
Mục phân loại 25.220.40. Lớp mạ kim loại
Trạng thái Có hiệu lực
Thay thế bằng
ASTM A 90/A 90M (2001)
Standard Test Method for Weight [Mass] of Coating on Iron and Steel Articles with Zinc or Zinc-Alloy Coatings
Số hiệu tiêu chuẩn ASTM A 90/A 90M
Ngày phát hành 2001-00-00
Mục phân loại 25.220.40. Lớp mạ kim loại
Trạng thái Có hiệu lực
Lịch sử ban hành
ASTM A 90/A 90M (2013)
Standard Test Method for Weight [Mass] of Coating on Iron and Steel Articles with Zinc or Zinc-Alloy Coatings
Số hiệu tiêu chuẩn ASTM A 90/A 90M
Ngày phát hành 2013-00-00
Mục phân loại 25.220.40. Lớp mạ kim loại
Trạng thái Có hiệu lực
* ASTM A 90/A 90M (2011)
Standard Test Method for Weight [Mass] of Coating on Iron and Steel Articles with Zinc or Zinc-Alloy Coatings
Số hiệu tiêu chuẩn ASTM A 90/A 90M
Ngày phát hành 2011-00-00
Mục phân loại 25.220.40. Lớp mạ kim loại
Trạng thái Có hiệu lực
* ASTM A 90/A 90M (2009)
Standard Test Method for Weight [Mass] of Coating on Iron and Steel Articles with Zinc or Zinc-Alloy Coatings
Số hiệu tiêu chuẩn ASTM A 90/A 90M
Ngày phát hành 2009-00-00
Mục phân loại 25.220.40. Lớp mạ kim loại
Trạng thái Có hiệu lực
* ASTM A 90/A 90M (2007)
Standard Test Method for Weight [Mass] of Coating on Iron and Steel Articles with Zinc or Zinc-Alloy Coatings
Số hiệu tiêu chuẩn ASTM A 90/A 90M
Ngày phát hành 2007-00-00
Mục phân loại 25.220.40. Lớp mạ kim loại
Trạng thái Có hiệu lực
* ASTM A 90/A 90M (2006)
Standard Test Method for Weight [Mass] of Coating on Iron and Steel Articles with Zinc or Zinc-Alloy Coatings
Số hiệu tiêu chuẩn ASTM A 90/A 90M
Ngày phát hành 2006-00-00
Mục phân loại 25.220.40. Lớp mạ kim loại
Trạng thái Có hiệu lực
* ASTM A 90/A 90M (2001)
Standard Test Method for Weight [Mass] of Coating on Iron and Steel Articles with Zinc or Zinc-Alloy Coatings
Số hiệu tiêu chuẩn ASTM A 90/A 90M
Ngày phát hành 2001-00-00
Mục phân loại 25.220.40. Lớp mạ kim loại
Trạng thái Có hiệu lực
* ASTM A 90/A 90M (1995)
Standard Test Method for Weight [Mass] of Coating on Iron and Steel Articles with Zinc or Zinc-Alloy Coatings
Số hiệu tiêu chuẩn ASTM A 90/A 90M
Ngày phát hành 1995-00-00
Mục phân loại 25.220.40. Lớp mạ kim loại
Trạng thái Có hiệu lực
* ASTM A 90/A 90M (1993)
Test Method for Weight (Mass) of Coating on Iron and Steel Articles with Zinc or Zinc-Alloy Coatings
Số hiệu tiêu chuẩn ASTM A 90/A 90M
Ngày phát hành 1993-00-00
Mục phân loại 25.220.40. Lớp mạ kim loại
Trạng thái Có hiệu lực
* ASTM A 90/A 90Ma (1995)
Standard Test Method for Weight [Mass] of Coating on Iron and Steel Articles with Zinc or Zinc-Alloy Coatings
Số hiệu tiêu chuẩn ASTM A 90/A 90Ma
Ngày phát hành 1995-00-00
Mục phân loại 25.220.40. Lớp mạ kim loại
Trạng thái Có hiệu lực
* ASTM A 90 (1981)
Test Method for Weight of Coating on Zinc-Coated (Galvanized) Iron or Steel Articles
Số hiệu tiêu chuẩn ASTM A 90
Ngày phát hành 1981-00-00
Mục phân loại 77.140.50. Sản phẩm và bán sản phẩm thép tấm
Trạng thái Có hiệu lực
Từ khóa
Coated * Coatings * Electrical engineering * Iron * Materials * Steel products * Steels * Testing * Weights * Zinc coatings
Số trang
4