Minimizing Stress-Corrosion in Wrought Heat-Treatable Aluminum Alloy Products

SAE ARP 823D

Số trang:
Ngày phát hành: 1997-03-01

Liên hệ

Tóm tắt
Chi tiết

The purpose of this recommended practice is to provide the aerospace industry with recommendations concerning minimizing of stress-corrosion cracking (SCC) in wrought high-strength aluminum alloy products. The detailed recommendations are based on practical engineering experience and reflect those design practices and fabricating procedures which have been found to be most effective in minimizing stress-corrosion cracking in wrought high-strength aluminum alloy products. This ARP provides general guidelines. For further information see references in 4.3.

Số hiệu tiêu chuẩn

SAE ARP 823D

Tên tiêu chuẩn

Minimizing Stress-Corrosion in Wrought Heat-Treatable Aluminum Alloy Products

Ngày phát hành

1997-03-01

Trạng thái

Hết hiệu lực

Tiêu chuẩn tương đương

Tiêu chuẩn liên quan

ASTM G 64 (1991) * MSFC-SPEC-522B (1987-07-01) * MIL-HDBK-5 * MIL-STD-1568

Thay thế cho

SAE ARP 823C (1988-10)

Thay thế bằng

SAE ARP 823E (2007-11-19)

Lịch sử ban hành

SAE ARP 823E (2007-11-19) * SAE ARP 823C (1988-10) * SAE ARP 823D (1997-03-01)

Từ khóa

Aerospace transport * Aluminium alloys * Stress corrosion * Air transport

Mục phân loại

49.025.20. Nhôm

Số trang

LOẠI TIÊU CHUẨN PHỔ BIẾN | TẤT CẢ LOẠI TIÊU CHUẨN

Classification of the Resistance to Stress-Corrosion Cracking of Heat-Treatable Aluminum Alloys
Số hiệu tiêu chuẩn	ASTM G 64
Ngày phát hành	1991-00-00
Mục phân loại	77.120.10. Nhôm và hợp kim nhôm
Trạng thái	Có hiệu lực

Minimizing Stress-Corrosion in Wrought Heat Treatable Aluminum Alloy Products
Số hiệu tiêu chuẩn	SAE ARP 823C
Ngày phát hành	1988-10-00
Mục phân loại	49.025.20. Nhôm
Trạng thái	Có hiệu lực

Minimizing Stress-Corrosion in Wrought Heat-Treatable Aluminum Alloy Products
Số hiệu tiêu chuẩn	SAE ARP 823E
Ngày phát hành	2007-11-19
Mục phân loại	49.025.20. Nhôm
Trạng thái	Có hiệu lực